polished bright surface 431 Stainless Steel Round Bar
-
Payment
-
Origin
China Mainland
-
Minimum Order
1
-
Packing
Pieces
- Contact Now Start Order
- Description
Product Detail
SASA Metal is 431 Stainless Steel Round Bar manufacturer and suppliers in china, specialized in the research, development and production of 431 Stainless Steel Round Bar;
Type 431 martensitic stainless steel,ASTM A276,431SS,AISI 431,T431 SS,UNS S43100,16Chromium with Ni Ferritic stainless steel bar include,410 Stainless Steel Round Bar,416 Stainless Steel Round Bar,420 Stainless Steel Round Bar,440C Stainless Steel Round Bar,ss 410 round bar
C% |
Si% |
Mn% |
P% |
S% |
Cr% |
Ni% |
N% |
Mo% |
Cu% |
=0.20 |
=1.0 |
=1.0 |
=0.040 |
=0.030 |
15.0-17.0 |
1.25-2.50 |
-- |
- |
-- |
T*S |
Y*S |
Hardness |
Elongation |
|
(Mpa) |
(Mpa) |
HRB |
HB |
(%) |
=415 |
=207 |
-- |
-- |
=45 |
Stainless Steel Round Bar products from SASA Metal:
431 Stainless Steel Round Bar manufacturers |
431 Stainless Steel Round Bar suppliers |
431 Stainless Steel Round Bar for sale |
431 Stainless Steel Round Bar price |
Specifications of 431 ss bar:
Standard |
ASTM A276, A484, A479, A580, A582, JIS G4303, JIS G4311,DIN 1654-5,DIN 17440,KS D3706,GB/T 1220 |
Material |
201,202,205,XM-19 etc. |
Surface |
Bright,Polishing,Pickled,Peeled,Black,Grinding,Hairline etc |
Technology |
Cold Drawn,Hot Rolled,Forged |
Specifications |
Size: 3mm~400mm |
Tolerance |
H9, H11, H13, K9, K11, K13 or as required |
More grade details of stainless steel shafts:
Type |
Grade |
Grade |
Chemical Component % |
||||||||||
C |
Cr |
Ni |
Mn |
P |
S |
Mo |
Si |
Cu |
N |
Other |
|||
Austenitic stainless steel |
201 |
1Cr17Mn6Ni5N |
=0.15 |
16.00-18.00 |
3.50-5.50 |
5.50-7.50 |
=0.060 |
=0.030 |
- |
=1.00 |
- |
=0.25 |
- |
201L |
03Cr17Mn6Ni5N |
=0.030 |
16.00-18.00 |
3.50-5.50 |
5.50-7.50 |
=0.060 |
=0.030 |
|
=1.00 |
|
=0.25 |
|
|
202 |
1Cr18Mn8Ni5N |
=0.15 |
17.00-19.00 |
4.00-6.00 |
7.50-10.00 |
=0.060 |
=0.030 |
|
=1.00 |
- |
=0.25 |
- |
|
204 |
03Cr16Mn8Ni2N |
=0.030 |
15.00-17.00 |
1.50-3.50 |
7.00-9.00 |
|
|
|
|
|
0.15-0.30 |
|
|
|
1Cr18Mn10Ni5Mo3N |
=0.10 |
17.00-19.00 |
4.00-6.00 |
8.50-12.00 |
|
|
2.80-3.50 |
|
|
0.20-0.30 |
|
|
|
2Cr13Mn9Ni4 |
0.15-0.25 |
12.00-14.00 |
3.70-5.00 |
8.00-10.00 |
|
|
|
|
|
|
|
|
|
2Cr15Mn15Ni2N |
0.15-0.25 |
14.00-16.00 |
1.50-3.00 |
14.00-16.00 |
|
|
|
|
|
0.15-0.30 |
|
|
|
1Cr18Mn10Ni5Mo3N |
=0.15 |
17.00-19.00 |
4.00-6.00 |
8.50-12.00 |
=0.060 |
=0.030 |
2.8-3.5 |
=1.00 |
- |
0.20-0.30 |
- |
|
301 |
1Cr17Ni7 |
=0.15 |
16.00-18.00 |
6.00-8.00 |
=2.00 |
=0.065 |
=0.030 |
- |
=1.00 |
- |
- |
- |
|
302 |
1Cr18Ni9 |
=0.15 |
17.00-19.00 |
8.00-10.00 |
=2.00 |
=0.035 |
=0.030 |
- |
=1.00 |
- |
- |
- |
|
303 |
Y1Cr18Ni9 |
=0.15 |
17.00-19.00 |
8.00-10.00 |
=2.00 |
=0.20 |
=0.030 |
1) |
=1.00 |
- |
- |
- |
|
303se |
Y1Cr18Ni9Se |
=0.15 |
17.00-19.00 |
8.00-10.00 |
=2.00 |
=0.20 |
=0.030 |
- |
=1.00 |
- |
- |
Se=0.15 |
|
304 |
0Cr18Ni9 |
=0.07 |
17.00-19.00 |
8.00-10.00 |
=2.00 |
=0.035 |
=0.030 |
- |
=1.00 |
- |
- |
- |
|
304L |
00Cr19Ni10 |
=0.030 |
18.00-20.00 |
8.00-10.00 |
=2.00 |
=0.035 |
=0.030 |
- |
=1.00 |
- |
- |
- |
|
304N1 |
0Cr19Ni9N |
=0.08 |
18.00-20.00 |
7.00-10.50 |
=2.00 |
=0.035 |
=0.030 |
- |
=1.00 |
- |
0.10-0.25 |
- |
|
304N2 |
0Cr18Ni10NbN |
=0.08 |
18.00-20.00 |
7.50-10.50 |
=2.00 |
=0.035 |
=0.030 |
- |
=1.00 |
- |
0.15-0.30 |
Nb=0.15 |
|
304LN |
00Cr18Ni10N |
=0.030 |
17.00-19.00 |
8.50-11.50 |
=2.00 |
=0.035 |
=0.030 |
- |
=1.00 |
- |
0.12-0.22 |
- |
|
305 |
1Cr18Ni12 |
=0.12 |
17.00-19.00 |
10.50-13.00 |
=2.00 |
=0.035 |
=0.030 |
- |
=1.00 |
- |
- |
- |
|
309S |
0Cr23Ni13 |
=0.08 |
22.00-24.00 |
12.00-15.00 |
=2.00 |
=0.035 |
=0.030 |
- |
=1.00 |
- |
- |
- |
|
310S |
0Cr25Ni20 |
=0.08 |
24.00-26.00 |
19.00-22.00 |
=2.00 |
=0.035 |
=0.030 |
- |
=1.00 |
- |
- |
- |
|
316 |
0Cr17Ni12Mo2 |
=0.08 |
16.00-18.50 |
10.00-14.00 |
=2.00 |
=0.035 |
=0.030 |
2.00-3.00 |
=1.00 |
- |
- |
- |
|
|
1Cr18Ni12Mo2Ti6) |
=0.12 |
16.00-19.00 |
11.00-14.00 |
=2.00 |
=0.035 |
=0.030 |
1.80-2.50 |
=1.00 |
- |
- |
Ti5(C%-0.02)~0.08 |
|
|
0Cr18Ni12Mo2Ti |
=0.08 |
16.00-19.00 |
11.00-14.00 |
=2.00 |
=0.035 |
=0.030 |
1.80-2.50 |
=1.00 |
- |
- |
Ti5*C%-0.70 |
|
316L |
00Cr17Ni14Mo2 |
=0.030 |
16.00-18.00 |
12.00-15.00 |
=2.00 |
=0.035 |
=0.030 |
2.00-3.00 |
=1.00 |
- |
- |
- |
316N |
0Cr17Ni12Mo2N |
=0.08 |
16.00-18.00 |
10.00-14.00 |
=2.00 |
=0.035 |
=0.030 |
2.00-3.00 |
=1.00 |
- |
0.10-0.22 |
- |
|
316N |
00Cr17Ni13Mo2N |
=0.030 |
16.00-18.50 |
10.50-14.50 |
=2.00 |
=0.035 |
=0.030 |
2.00-3.00 |
=1.00 |
- |
0.12-0.22 |
- |
|
316J1 |
0Cr18Ni12Mo2Cu2 |
=0.08 |
17.00-19.00 |
10.00-14.50 |
=2.00 |
=0.035 |
=0.030 |
1.20-2.75 |
=1.00 |
1.00-2.50 |
- |
- |
|
316J1L |
00Cr18Ni14Mo2Cu2 |
=0.030 |
17.00-19.00 |
12.00-16.00 |
=2.00 |
=0.035 |
=0.030 |
1.20-2.75 |
=1.00 |
1.00-2.50 |
- |
- |
|
317 |
0Cr19Ni13Mo3 |
=0.12 |
18.00-20.00 |
11.00-15.00 |
=2.00 |
=0.035 |
=0.030 |
3.00-4.00 |
=1.00 |
- |
- |
- |
|
317L |
00Cr19Ni13Mo3 |
=0.08 |
18.00-20.00 |
11.00-15.00 |
=2.00 |
=0.035 |
=0.030 |
3.00-4.00 |
=1.00 |
- |
- |
- |
|
|
1Cr18Ni12Mo3Ti6 |
=0.12 |
16.00-19.00 |
11.00-14.00 |
=2.00 |
=0.035 |
=0.030 |
2.50-3.50 |
=1.00 |
- |
- |
Ti5(C%-0.02)~0.08 |
|
|
0Cr18Ni12Mo3Ti |
=0.08 |
16.00-19.00 |
11.00-14.00 |
=2.00 |
=0.035 |
=0.030 |
2.50-3.50 |
=1.00 |
- |
- |
Ti5*C%-0.70 |
|
317J1 |
0Cr18Ni16Mo5 |
=0.040 |
16.00-19.00 |
15.00-17.00 |
=2.00 |
=0.035 |
=0.030 |
4.00-6.00 |
=1.00 |
- |
- |
- |
|
321 |
1Cr18Ni9Ti6 |
=0.12 |
17.00-19.00 |
8.00-11.00 |
=2.00 |
=0.035 |
=0.030 |
- |
=1.00 |
- |
- |
Ti5(C%-0.02)~0.08 |
|
|
0Cr18Ni10Ti |
=0.08 |
17.00-19.00 |
9.00-12.00 |
=2.00 |
=0.035 |
=0.030 |
- |
=1.00 |
- |
- |
Ti=5*C% |
|
347 |
0Cr18Ni11Nb |
=0.08 |
17.00-19.00 |
9.00-13.00 |
=2.00 |
=0.035 |
=0.030 |
- |
=1.00 |
- |
- |
Nb=10*C% |
|
XM7 |
0Cr18Ni9Cu3 |
=0.08 |
17.00-19.00 |
8.50-10.50 |
=2.00 |
=0.035 |
=0.030 |
- |
=1.00 |
3.00-4.00 |
- |
- |
|
XM15J1 |
0Cr18Ni13Si4 |
=0.08 |
15.00-20.00 |
11.50-15.00 |
=2.00 |
=0.035 |
=0.030 |
- |
3.00-5.00 |
- |
- |
2) |
|
Austenite |
329J1 |
0Cr26Ni5Mo2 |
=0.08 |
23.00-28.00 |
3.00-6.00 |
=1.50 |
=0.035 |
=0.030 |
1.00-3.00 |
=1.00 |
- |
- |
2) |
|
1Cr18Ni11Si4AlTi |
0.10-0.18 |
17.50-19.50 |
10.--120.. |
=0.80 |
=0.035 |
=0.030 |
- |
3.40-4.00 |
- |
- |
Al 0.10-0.30; Ti 0.40-0.70 |
|
|
00Cr18Ni5MoSi2 |
=0.030 |
18.00-19.50 |
4.50-5.50 |
1.00-2.00 |
=0.035 |
=0.030 |
2.50-3.00 |
1.30-2.00 |
- |
- |
- |
|
Ferrite Stainless Steel |
405 |
0Cr13Al |
=0.08 |
11.50-14.50 |
3) |
=1.00 |
=0.035 |
=0.030 |
- |
=1.00 |
- |
- |
Al 0.10-0.30 |
410L |
00Cr12 |
=0.030 |
11.00-13.00 |
3) |
=1.00 |
=0.035 |
=0.030 |
- |
=1.00 |
- |
- |
- |
|
430 |
1Cr17 |
=0.12 |
16.00-18.00 |
3) |
=1.25 |
=0.035 |
=0.030 |
- |
=0.75 |
- |
- |
- |
|
430F |
Y1Cr17 |
=0.12 |
16.00-18.00 |
3) |
=1.00 |
=0.035 |
=0.15 |
1) |
=1.00 |
- |
- |
- |
|
434 |
1Cr17Mo |
=0.12 |
16.00-18.00 |
3) |
=1.00 |
=0.035 |
=0.030 |
0.75-1.25 |
=1.00 |
- |
- |
- |
|
447J1 |
00Cr30Mo2 |
=0.010 |
28.50-32.00 |
- |
=0.40 |
=0.035 |
=0.030 |
1.50-2.50 |
=0.40 |
- |
=0.015 |
- |
|
XM27 |
00Cr27Mo |
=0.010 |
25.00-27.50 |
- |
=0.40 |
=0.035 |
=0.030 |
0.75-1.50 |
=0.40 |
- |
=0.015 |
- |
Martensite stainless steel |
403 |
1Cr12 |
=0.15 |
11.50-13.00 |
3) |
=1.00 |
=0.035 |
=0.030 |
- |
=0.50 |
- |
- |
- |
410 |
1Cr13 |
=0.15 |
11.50-13.50 |
3) |
=1.00 |
=0.035 |
=0.030 |
- |
=1.00 |
- |
- |
- |
|
405 |
0Cr13 |
=0.08 |
11.50-13.50 |
3) |
=1.00 |
=0.035 |
=0.030 |
- |
=1.00 |
- |
- |
- |
|
416 |
Y1Cr13 |
=0.15 |
12.00-14.00 |
3) |
=1.25 |
=0.035 |
=0.15 |
1) |
=1.00 |
- |
- |
- |
|
410J1 |
1Cr13Mo |
=0.08-0.18 |
11.50-14.00 |
3) |
=1.00 |
=0.035 |
=0.030 |
0.30-0.60 |
=0.60 |
- |
- |
- |
|
420J1 |
2Cr13 |
0.16-0.25 |
12.00-14.00 |
3) |
=1.00 |
=0.035 |
=0.030 |
- |
=1.00 |
- |
- |
- |
|
420J2 |
3Cr13 |
0.26-0.35 |
12.00-14.00 |
3) |
=1.00 |
=0.035 |
=0.030 |
- |
=1.00 |
- |
- |
- |
|
420F |
Y3Cr13 |
0.26-0.40 |
12.00-14.00 |
3) |
=1.25 |
=0.035 |
=0.15 |
1) |
=1.00 |
- |
- |
- |
|
|
3Cr13Mo |
0.28-0.35 |
12.00-14.00 |
3) |
=1.00 |
=0.035 |
=0.030 |
0.50-1.00 |
=0.80 |
- |
- |
- |
|
|
4Cr13 |
0.36-0.45 |
12.00-14.00 |
3) |
=0.80 |
=0.035 |
=0.030 |
- |
=0.60 |
- |
- |
- |
|
431 |
1Cr17Ni2 |
0.11-0.17 |
16.00-18.00 |
1.50-2.50 |
=0.80 |
=0.035 |
=0.030 |
- |
=0.80 |
- |
- |
- |
|
440A |
7Cr17 |
0.60-0.75 |
16.00-18.00 |
3) |
=1.00 |
=0.035 |
=0.030 |
4) |
=1.00 |
- |
- |
- |
|
440B |
8Cr17 |
0.75-0.95 |
16.00-18.00 |
3) |
=1.00 |
=0.035 |
=0.030 |
4) |
=1.00 |
- |
- |
- |
|
|
9Cr18 |
0.90-1.00 |
17.00-19.00 |
3) |
=0.80 |
=0.035 |
=0.030 |
4) |
=0.80 |
- |
- |
- |
|
440C |
11Cr17 |
0.95-1.20 |
16.00-18.00 |
3) |
=1.00 |
=0.035 |
=0.030 |
4) |
=1.00 |
- |
- |
- |
|
440F |
Y11Cr17 |
0.95-1.20 |
16.00-18.00 |
3) |
=1.25 |
=0.035 |
=0.15 |
4) |
=1.00 |
- |
- |
- |
|
|
9Cr18Mo |
0.95-1.10 |
16.00-18.00 |
3) |
=0.80 |
=0.035 |
=0.030 |
0.40-0.70 |
=0.80 |
- |
- |
- |
|
|
9Cr18MoV |
0.85-0.95 |
17.00-19.00 |
3) |
=0.80 |
=0.035 |
=0.030 |
1.00-1.30 |
=0.80 |
- |
- |
V0.07-0.12 |
|
PH Stainless Steel |
630 |
0Cr17Ni4Cu4Nb |
=0.07 |
15.50-17.50 |
6.50-7.50 |
=1.00 |
=0.035 |
=0.030 |
- |
=1.00 |
3.00-5.00 |
- |
Nb 0.15-0.45 |
631 |
0Cr17Ni7Al |
=0.09 |
16.00-18.00 |
6.50-7.50 |
=1.00 |
=0.035 |
=0.030 |
- |
=1.00 |
=0.50 |
- |
Al 0.75-1.50 |
|
632 |
0Cr15Ni7Mo2Al |
=0.09 |
14.00-16.00 |
6.50-7.50 |
=1.00 |
=0.035 |
=0.030 |
2.00-3.00 |
=1.00 |
- |
- |
Al 0.75-1.50 |
Stainless Steel Round Bar Packaging:
SASA Metal 431 Stainless Steel Round Bar are packed and labeled according to the regulations and customer's requests. Great care is taken to avoid any damage which might otherwise be caused during storage or transportation.
410 Stainless Steel Round Bar manufacturers |
410 Stainless Steel Round Bar suppliers |
410 Stainless Steel Round Bar for sale |
410 Stainless Steel Round Bar price |
- Hot Rolled Pickled Cold Drawn 321 Stainless Steel Round Bars 1 Pieces / (Min. Order)
- SUS hairline brush 310 Stainless Steel Round Bar 1 Pieces / (Min. Order)
- Polished bright surface 316 Stainless Steel Round Bar 1 Pieces / (Min. Order)
- 201 304L 316 316L 304 polished stainless steel round bar 1 Pieces / (Min. Order)